Which ASTM A573 welding structural steel is the best?

The company has five major departments: steel plate production department (including quality inspection team), sales department, market development department, after-sales and logistics department, and finance department. The backbone of steel business from all over the country, with the chairman as the core, integrates self-confidence, independence, passion and responsibility, and strives for excellence! All people share the same belief: "Being a refined steel product line rewards customers, strengthen the steel industry, and realize the corporate dream!

The mechanical properties of 20MnV steel are as follows: tensile strength 785 MPa, yield strength 590 MPa, elongation after fracture 10%, reduction of area 40%, impact absorption energy 55 J. ASTM A573 welding structural steel, 20MnV steel has good properties, good strength, toughness and plasticity, good hardenability and machinability. After carburizing, 20MnV steel can be directly quenched without secondary quenching to improve the core structure. The weldability of 20MnV steel is good, but there is temper brittleness at 300-360 ℃ during heat treatment.

asme sa514 grade H alloy steel coil element composition%
C: 0.12-0.21, Si: 0.20-0.35, Mn: 0.95-1.30, P max.: 0.035, S max.: 0.035, Cr: 0.40-0.65, Ni: 0.30-0.70, Mo: 0.20-0.30, V: 0.03-0.08, B: 0.001-0.005
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

Both parties shall confirm the ASTM A573 welding structural steel material object and the quality of the products, confirm the reasons for the defects and the quality of the products, and sign the quality inspection agreement. Major quality objections shall be reported to relevant leaders in a timely manner, and shall be discussed and solved with the ASTM A573 welding structural steel steel plant.