A573 Grade 65 steel density annual output

Established in 2014, Steel Safety Day was set up to reinforce awareness of the five most common causes of safety incidents and to create a safer working environment across the entire steel industry worldwide. By focusing every year on the five causes - moving machinery, working at heights, falling objects, on-site traffic and A573 Grade 65 steel density process safety incidents - worldsteel intends to set up a continuous improvement process and reiterate its commitment to the safety and health of the people who work in the A573 Grade 65 steel density industry.

Generally speaking, the higher the strength of A573 Grade 65 steel density, weathering steel, the greater the hardness, while the plasticity and toughness will decrease. When the carbon content of weathering steel exceeds 1.2%, the hardness will increase, but the strength will not increase, but will decrease. Resilience will also decline quickly. When the carbon content is high, the cementite increases and forms network distribution, which weakens the connection between grains and makes the mechanical properties of steel worse.

A514 gr K quenched and tempered alloy steel chemical composition (melting analysis)%
C: 0.10-0.20, Si: 0.15-0.30, Mn: 1.10-1.50, P max.: 0.035, S max.: 0.035, Mo: 0.45-0.6.0, B: 0.001-0.005
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

"Hard and solid, honest commitment, practical effect". To strive for a solid enterprise foundation with hard work style; to promise first-class enterprise service with honest faith; to create efficient enterprise performance with practical spirit.