A633Gr.D as-rolled material carbon steel plates

The company has the industry's advanced automated production lines and precision laboratory instruments and a capable steel industry management team. Through scientific management, optimized technology, and rigorous testing, the company will keep the production efficiency and production quality at the leading level in the industry and continue to provide customers with high-quality A633Gr.D as-rolled material products. At the same time, the company is committed to building a comprehensive steel manufacturing industry and strives to make the company leads new progress and development.

S45C steel plate chemical composition: C 0.42~0.48, Si 0.15~0.35, Mn 0.60~0.90, P≤0.030, S≤0.035, Cu≤0.30, Ni≤0.20, Cr≤0.20
Mechanical properties of A633Gr.D as-rolled material product
Tensile strength>686MPa
Yield strength>490MPa
Elongation δ5>17%
Shrinkage ψ>45%
Impact toughness value>78J/cm2
The hardness is 201~269HB.

Chemical composition(%) of A213 T36 steel pipe(Carbon: 0.10–0.17, Manganese: 0.80–1.20, Phosphorus: 0.03, Sufur: 0.025, Silicon: 0.25–0.50, Nickel: 1.00–1.30, Chromium: 0.3, Molybdenum: 0.25–0.50, Vanadium: 0.02, Niobium: 0.015–0.045, Nitrogen: 0.02, Aluminum: 0.05, Cu 0.50–0.80). Mechanical properties for A633Gr.D as-rolled material, A213 T36 steel pipe: Tensile strength(min): 415Mpa; Yield strength(min): 205Mpa; Elongation: 30%; Hardness, HB: 163max.

The hot rolling method is to heat the A633Gr.D as-rolled material steel material to about 1000 ℃ ~ 1250 ℃ and use the rolling mill to roll it. The traditional hot rolling process is generally divided into the following two steps: the first step is to use the primary rolling mill or billet rolling mill to roll the ingot, billet or continuous casting billet into a certain shape and size of billet. This kind of A633Gr.D as-rolled material rolling process is usually called semi-finished product production, also called blank production.

Compared with other fast-moving consumer goods, steel consumption is obviously different, with a wide range of use and a long service life. Therefore, the quality and service of steel materials are particularly important. Service is always one of our top concerns, especially after-sales service. We have mature after-sales service team, and can help you solve problems professionally during application of the steel materials.

We had a wonderful trip in Phuket Island, Thailand. At the end of 2019, in order to thank employees for their hard work for a year and enrich their lives, our company organized a pleasant trip to Phuket Island, Thailand. The tour lasted 6 days and 5 nights, and returned by plane on the evening of December 27. We took off in Zhengzhou at about 5 o'clock in the afternoon on the 22th December.