structural steel shapes A36 top manufacturer in Hongkong

Q370R Pressure Vessel Steel: Steel used to manufacture pressure vessels in petrochemical, gas separation, gas storage and transportation equipment. It is required to have sufficient strength and toughness, good welding performance and hot and cold processing performance. The commonly used steels are mainly low-alloy high-strength steel and carbon steel. Q370R implements the domestic standard GB713-2008.

A514 grade Q alloy structural steel chemical composition (melting analysis)%
C: 0.14-0.21, Si: 0.15-0.35, Mn: 0.95-1.30, P max.: 0.035, S max.: 0.035, Ni: 1.20-1.50, Cr: 1.00-1.50, Mo: 0.45-0.6.0, V: 0.03-0.08
The mechanical properties in thickness (mm)T≤65
Yield strength (≥Mpa): 690
Tensile strength (Mpa):760-895
Elongation in ≥,%: 18

Our quality and service commitment: product quality problems, life-long replacement.In the process of using, any time if you find we supplied steel materials not conform to the requirements of technical standards, we can replace it for you free of charge. However, it should be noted that non product quality problems caused by improper use are not covered by the warranty. Please pay attention to the service time commitment as well as the product quality assurance commitment. Because only the products of big brands and reliable enterprises with complete after-sales service system can truly realize the long-term product quality assurance and the whole process of service.

Our 1810mm production line successfully rolled 1.2mm × 1250mm ultra-thin specifications high strength automotive steel, and the product quality and performance fully met the standards. In recent years, customers have become increasingly demanding for lightweight vehicles. Our company aims at the market and focuses on the development of thin-gauge high strength automotive structural steel shapes A36 steel. The research and development personnel adjusted the product composition based on theoretical calculations and drawing on other experiences to meet customers' higher requirements for automotive steel yield strength and tensile strength.